http://www.gurit.com/page.asp?section=00010001007100030006§ionTitle=Previous+Projects+utilising+composites+from+Gurit Run it by these...
Coosa bluewater 26 should be fine for a transom.
LMAO and Thank you.
Here is a Vinylester hull with 1' Corecell bagged in Corebond (polyester putty) NO Problem if you read the can! [IMG]...
First of all you are NOT fairing the surface just abrading it and need only to break the shine is all,a sanding block it the wrong tool to use,a...
Mat? Do a test and see if the binder breaks down in your epoxy,you will still need to give the epoxy a toe hold some scotch brite or the like.
you are going to figure out a way,sponge backed sanding pad, Red Scotch brite, flap wheel ,there is a way without grinding down the laminate and...
the Duratec primer comes White Grey and black. the one I use is the Grey 707 002
http://www.westsystem.com/ss/polyester-over-epoxy/
Do a test, it is the Amine blush that poisons the polymer reaction and soap and water will remove it, Not a solvent. The rules seem to be, cured...
I would try to get the bulkheads/floors in your case close as I could ,just add some material to the top. Gelcoat! you could do a soap and water...
What is the problem? it is done everyday building VE boats,Excellent secondary bonding.
Most of us have our own systems,But it would be worth a try, maybe someone needs a infusion setup.
You should be OK with that,no harm in a little overbuild,remember you are using glass in the best possible way. Now just work out your hard points...
Composites one and I usually use CCP material.
The old Rotex which was the standard is not sold anymore.
Teak, Chinese built ships with it ,then the Britts.
I have used the CR 3400 from SP in the past with great results.
You will need to drill a few holes to find the extent of the water intrusion.
I would use a filled Epoxy system to get the shrinkage @ nil,West 404 filler would be one choice.