Biggest OB I’ve seen are 150hp so 105 hp at the jet so two would be close. Hole shot power is slow to respond when compared to a prop. Add in a...
This is awesome. I’m kinda doing the same thing. Modified V. I was playing with the radius on some models. So I understand what you mean.good...
Take a piece of left over cut off from the hull that has these voids and do a post cure on it. Take macro photos before and after. See what happens.
Here is a non modified and modified bow
Hi thank you,sides approx 21"533mm beam approx 65"~70" 1650mm + In the pic you can see the beam narrows as you get to the bow,was going to add on...
Deering thx for the help, car topper so 9.9 is why. Any thoughts on how to cut the ply. Is it as simple as one cut down the 0 axis maybe 30” or...
Keeping the floor flat where the bend starts is the goal.Id assume I would get a little V or deadrise at that point.I haven't tried 3/8 yet. That...
Hope this works. So the kerfs would have to be right we’re the transition starts. That seems to be where the most twist is. Would I need kerfs in...
Yes that will help.Thx. I’ve only played with Mylar so far as to where and how to cut the floor to shape the V. I’ll find a pic of what I’m...
I’ve had the aluminum version 1648 and it’s worked well for what I do. I’ve since sold the boat and need to build myself a new one this time...
Noah’s in Eastern Canada may have it
Not sure the 12 lb density foam will compress that easily. May have to cut rebates for the tape not sure. Epoxy will be my resin. Looks like I...
Thx Phil,ya I agree building out of ply would be easier.I have enough of these foam panels for a 14'boat ,if I dont use them now my fear is they...
I have some 1400mmx450mmx12mm corecell A 1200 cut offs i^d like to laminate together.What is the best way to join the long sides together?This is...
I think the one I used was 50%. You’ll have to try a few and see. Remember resin viscosity will half with a 10c increase in temp. So keep the goo...
I get the same peel results Fall man,a thin biax skin separates, its only when i peel test a thicker skin like 4 layers 12oz thats when the whole...
Yes, practice on some small scraps first. Then you'll understand.
In the not to far off future,you'll just say,Hey Siri or Alexa, what does this weigh.Until then i cant help ya.
Should work just fine, this way you keep the resin in the part ,not throw it away with the flow media.Perimeter feed with center vac would be my...
do a search here,Composites Central Forum - The #1 forum for composites discussion http://www.compositescentral.com/ Ive learned quite a few...